立式喷涂，效率致胜

字體(tǐ)大小(xiǎo)：小(xiǎo)中(zhōng)大

本期将带您了解静電(diàn)粉末喷涂工(gōng)艺及中(zhōng)联铝业新(xīn)引入设备——立式喷涂

广东中(zhōng)联铝业

立式喷涂设备

What is the Powder Coating for aluminium profiles?

Powder coating is a dry surface treatment procedure. After the fine pigment particles are electrostatically treated, they are sprayed on the product to form a coating, which is solidified by a curing oven to form a solid coating. Nowadays, most of the coloured aluminium profiles on the market are achieved by powder coating. The coating thickness can reach 40~120 μm.

什么是铝型材粉末喷涂？

粉末喷涂是一种干燥的表面处理(lǐ)程序。将细颜料颗粒静電(diàn)处理(lǐ)后，将它们喷在产(chǎn)物(wù)上以形成涂层，该涂层被固化的烤箱固化以形成固體(tǐ)涂层。

如今，市场上的大多(duō)数彩色的铝型材都是通过粉末涂料来实现的。涂层厚度可(kě)以达到40〜120μm。

What are the advantages of Powder Coating for aluminium profiles?

1) The surface is beautiful, durable, scratch-resistant, chemically resistant to attack, and UV-resistant;

2) Environmental protection, no waste liquid discharge;

3) Perfect corner coverage;

4) Uniform colour and wide range of spray colours;

5) The thickness is easy to control and thus is widely used.

铝型材粉末喷涂的优势：

1、表面美观、耐用(yòng)、耐刮擦、耐化學(xué)侵蚀、耐紫外線(xiàn)；

2、环保，无废液排放；

3、完美角落覆盖；

4、颜色均匀，喷涂颜色范围广泛；

5、厚度易于控制，因此被广泛应用(yòng)。

外网资料拓展：

粉末涂料和涂层始于20世纪30年代。最初采用(yòng)的是将聚乙烯粉末通过火焰喷涂的方式涂在金属表面上，这是粉末涂料的开始。直到20世纪50年代，在德(dé)國(guó)发明了发明性的粉末床涂覆工(gōng)艺后，粉末涂料和涂层工(gōng)艺得到了极大的发展。

而中(zhōng)國(guó)开始比较晚。1989年，江苏常州华艺铝型材厂引进了美國(guó) Nordson 粉末涂装(zhuāng)设备，这是中(zhōng)國(guó)第一家铝粉末涂装(zhuāng)。随着经济改革和开放，粉末涂料技(jì )术在中(zhōng)國(guó)得到了大力发展。初期采用(yòng)的是横向生产(chǎn)線(xiàn)。但随着经济技(jì )术的发展，意大利和日本率先引进立式喷涂生产(chǎn)線(xiàn)并开始广泛应用(yòng)。立式粉末涂层生产(chǎn)線(xiàn)已经发展成為(wèi)成熟的产(chǎn)品，从预处理(lǐ)、干燥到粉末涂层的均匀性，再到固化效果，均已达到國(guó)外先进水平，由于立式線(xiàn)的占地面积小(xiǎo)，操作(zuò)人员数量少，喷涂的均匀性和固化层的效果均达到完美的结果。

操作(zuò)流程

粉末喷涂工(gōng)艺步骤：上架——酸洗——水洗——铬化——水洗——烘干——下架——上架——喷涂——固化——成品包装(zhuāng)

水洗：指对铝型材进行预处理(lǐ)前，先洗去附着于型材表面的杂质(zhì)油脂等，同时在表面形成水膜，避免与氧气接触；

铬化：铬酸盐处理(lǐ)，行业内称“铬化”，该工(gōng)艺影响后续型材表面附着力和耐腐蚀力；烘干：避免后续漆膜出现气泡、脱落等现象固化：粉末融化后，自流平形成永久性膜。